Influence Of Coating Process Of High‑Tenacity Yarn On Weaving Performance
High‑Tenacity Yarn is composite high‑strength yarn with inner core plus surface coating structure. Uniformity and adhesion of coating layer directly affect on‑machine performance of High‑Tenacity Yarn in subsequent weaving. Some footwear and webbing manufacturers get qualified tenacity test results, yet encounter fuzzing, coating peeling and tow dispersion during weaving. Process control level of coating serves as one non‑negligible inducementdixiangxcl....The inner core of High‑Tenacity Yarn usually adopts polyester or polyamide high‑strength filament, covered by functional coating colloid. Uneven coating thickness may expose base filament under high‑speed weaving friction where local coating is too thin. Excessive coating thickness stiffens yarn, raises running resistance of thread‑guiding parts and increases yarn‑breakage risk. Bonding force between colloid and core filament also matters. Insufficient adhesion causes peeling off after repeated friction, and debris accumulates inside looms and increases cleaning frequency.Downstream products set different requirements for coating layer of High‑Tenacity Yarn. Fly‑knit footwear fabric requires flexible and wear‑resistant coating to avoid powder dropping during knitting. Luggage webbing pays more attention to heat resistance of coating to fit subsequent hot‑press setting procedures.Raw‑material pretreatment, coating speed and drying‑curing temperature influence final coating effect during manufacturing. When switching denier specification of High‑Tenacity Yarn, complete coating parameters shall be adjusted instead of copying old process directly. Downstream purchasers are suggested to run small‑loom trial for new‑arrival High‑Tenacity Yarn and check coating wear resistance before mass‑volume production.Jiangsu Dixiang New Materials Technology Co., Ltd. operates multiple coating production lines and emphasizes coating‑procedure management for High‑Tenacity Yarn. It supplies matched‑specification High‑Tenacity Yarn for footwear, luggage and webbing scenarios and supports customer sample evaluation.